Sample results
The following micrographs illustrate typical dislocation etch pits on cleaved rock salt surfaces These images show a sample that was annealed after cleavage (no deliberate deformation) click to enlarge low mag image, click to enlarge high mag image. ![]() ![]() These images show a sample that was deformed and then annealed at 450°C for two hours. The onset of polygonization can be seen. (Sample courtesy of B. Close and J. Samuels) click to enlarge low mag image, click to enlarge high mag image. ![]() ![]() These images show a sample that was deformed and then annealed at 680°C for two hours. The sample is fully polygonized. (Sample courtesy of H. Stern and T. Rogers) click to enlarge low mag image, click to enlarge high mag image. Other Images ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge ![]() click to enlarge |
||||
|